Development and Characterization of Sisal Fiber Reinforced Polypropylene Composite Materials
348-358Megtekintések száma:380In most of the developing countries, plastic polypropylene is not fully recycled and converted in-to use after it is once used. Sisal fiber is also widely available in different developing countries like Ethiopia. Adding this two materials and developing automotive interior part was taken as a primary motive for it reduces cost and is environmentally friendly. Thus, the main purpose of this research is to develop composite material from natural fibre (sisal fiber) reinforced with recycled plastic waste (polypropylene) for interior automobile accessories specifically for internal door trim panel application. This research examines effect of fiber length, fiber loading and chemical treatment of fiber on the physical and chemical properties of the sisal fiber reinforced polypropylene (SFRPP) composite material. The waste polypropylene and the treated and untreated sisal fiber with variable length and weight ratio (fiber/matrix ratio) were mixed. Flammability of sisal fiber reinforced Polypropylene (SFRPP) composites material was examined by a horizontal burning test according to ASTM D635 and chemical resistance of the sisal fibre reinforced PP composites was studied using ASTM D543 testing method. The result on the flammability test shows that treated fiber has lower burning rate than untreated fiber and decreases with increase in fiber length and fiber loading. The resistance of the composites to water has increased as the fiber length increases and decreased as the fiber loading increase. Generally, SFRPP composite is found to have better resistance to water than NaOH and H2SO4 and treating the fiber has brought considerable improvement on chemical resistance of the composite. Fiber loading and fiber length has positive and negative effect on the flammability of the SFRPP composite respectively.
-
Adaptability of Powdered Activated Carbon Production from Ground Catering Waste Pyrolysis Coke
162-171Megtekintések száma:122Three mixture of catering waste was pyrolyzed at 650, 725 and 900 °C and the solid residue (coke) was examined for powdered activated carbon production. For this, the carbon content, iodine number, particle size distribution and scanning electron microscopic images were analysed. Based on the carbon content, these cokes are suitable for activated carbon production, which were 60-85 wt.% (depending on the base material and pyrolysis temperature). The studied cokes showed slightly porous structure with smooth surfaces. Because of this, the iodine number was mostly small (13-30). Based on the grinding experiments, 10 minutes of grinding was found to be optimal. After this grinding time, the reached iodine number of powdered activated carbon was 350-610.