Adaptability of Powdered Activated Carbon Production from Ground Catering Waste Pyrolysis Coke
162-171Megtekintések száma:131Three mixture of catering waste was pyrolyzed at 650, 725 and 900 °C and the solid residue (coke) was examined for powdered activated carbon production. For this, the carbon content, iodine number, particle size distribution and scanning electron microscopic images were analysed. Based on the carbon content, these cokes are suitable for activated carbon production, which were 60-85 wt.% (depending on the base material and pyrolysis temperature). The studied cokes showed slightly porous structure with smooth surfaces. Because of this, the iodine number was mostly small (13-30). Based on the grinding experiments, 10 minutes of grinding was found to be optimal. After this grinding time, the reached iodine number of powdered activated carbon was 350-610.
-
Hazai Ipari Hulladékok Innovatív Hasznosítási Lehetőségei Építőanyagipari Célra
203-212Megtekintések száma:120A Miskolci Egyetem Műszaki Földtudományi Karán működő Fenntartható Természeti Erőforrás Gazdálkodás Kiválósági Központban elvégzett kutatások eredményei azt mutatják, hogy a megfelelő előkészítést alkalmazva és a körülményeket optimálva a hulladék alapanyagok eljárástechnikai jellemzőinek (szemcseméret eloszlás, fajlagos felület) megváltoztatásával az építőanyag termékek fizikai és mechanikai tulajdonságai (szilárdság, tömörség) javíthatók. Kutatásaink ugyanis kimutatták, hogy a kémiai aktiválás mellett a mechanikai aktiválás is egy igen hatékony eszköz a tulajdonságok szabályozására. Ez azonban megváltoztatja nemcsak a termék fizikai, mechanikai, hanem a szerkezeti, ásványtani jellemzőit is, ezért ezen jellemzők meghatározása is kiemelten fontos.